EVALUATION OF MECHANICAL PROPERTIES OF PALM OIL FUEL ASH (POFA) BLENDED – GRANITE - GRAVEL CONCRETE


EVALUATION OF MECHANICAL PROPERTIES OF PALM OIL FUEL ASH (POFA) BLENDED – GRANITE - GRAVEL CONCRETE  

ABSTRACT

Utilizing Palm Oil Fuel Ash (POFA) in the concrete mix is a major way of turning waste to wealth. Gravel as an aggregate is cheaper than granite. Thus, obtaining an optimum combination of these materials in achieving a maximum compressive strength in concrete will go a long way in helping the construction industry. The study was carried out to establish an optimum replacement ratio for Palm Oil Fuel Ash (POFA) blended granite-gravel of concrete. A Uniform water/binder (w/b) ratio of 0.5 and mixes ratio of 1:2:4 was utilized. Thirteen runs of experiments plus control were designed using the Central Composite Response Surface method (Design Expert). Based on the analysis, the increase in granite volume led to increasing in compressive strength. However, increase in POFA percentage led to decrease in compressive strength at 7, 28, 56 and 90 days curing ages. The study also observed highest compressive strength at 25% POFA replacement and lowest at 35% replacement. Also, for granite, highest and lowest compressive strength were achieved at 100% and 0% replacement respectively. However, for slump height, the higher the percentage of granite or POFA in concrete, the higher the slump height. The optimization analysis showed that, at 29.69% POFA and 98.75% Granite, compressive strength of 24.29 N/mm2 and slump height of 89.36mm were achieved. The optimum strength found is slightly higher than the maximum strength achieved (24.27N/mm2) at 90 days and also, slightly lower than the control (25.33 N/mm2). 

TABLE OF CONTENTS

CERTIFICATION i

DEDICATION ii

ACKNOWLEDGEMENT iii

LIST OF TABLES vii

LIST OF FIGURES ix

ABSTRACT xi

CHAPTER ONE 1

INTRODUCTION 1

1.1 Background of the study 1

1.2 Scope 4

1.4 Justification 5

1.5 Statement of Problem 5

1.6 Aim 5

1.7 Objectives 5

CHAPTER TWO 6

LITERATURE REVIEW 6

2.1 Properties of concrete with POFA 6

2.1.1 Physical properties 6

2.1.2 Chemical Properties of POFA 7

2.1.3 Mechanical properties of POFA 8

2.2 Compressive Strength of Concrete with Replaced POFA 10

2.3 Ultrasonic Pulse Velocity (UPV) of Concrete with Replaced POFA 13

2.4 Workability of Concrete with Replaced POFA 14

2.5 Porosity of Concrete with Replaced POFA 16

2.6 Permeability of Concrete with Replaced POFA 18

2.7 Properties of Cement 19

2.7.1 Physical properties of Cement 19

    2.7.2Mechanical properties of Cement 20

    2.7.3Chemical Properties of Cement 20

   2.7.4Cement hydration 20

CHAPTER THREE 22

Study Area 22

3.0 Materials Used and Methodology 22

3.1. Materials 22

3.1.1 Cement 23

3.1.2 Aggregate 23

3.1.3 Granite 23

3.1.4 Gravel 23

3.1.5 Water 24

3.1.6 Palm Oil Fuel Ash (POFA) 24

3.2 Methodology 25

   3.2.1. Sieve Analysis Procedure 25

3.2.2 Specific Gravity of Ordinary Portland Cement Determination 26

3.2.2.1 Experimental Procedure 27

3.3: Concrete Mix Design 29

 3.4 Fresh Concrete Workability 30

3.5 Density 31

3.6 Determination of Compressive Strength 31

CHAPTER FOUR 33

RESULTS AND DISCUSSIONS 33

4.1 Oxides Composition of POFA 33

4.2 Grain size distributions from sieve analysis 34

4.3 Compressive Strength Test Results 35

4.4 Optimum Mix Ratio Determination 52

CHAPTER FIVE 53

CONCLUSION AND RECOMMENDATIONS 53

5.1 Conclusion 53

5.2 Recommendation 54

REFERENCES 55

LIST OF TABLES

Table2. 1: Chemical composition range of OPC and POFA 7

Table2. 2: Chemical composition analysis in POFA 8

Table2. 3: Compressive strength of concrete with various percentages of POFA 10

Table2. 4: Tensile strength of concrete by the addition of various % of POFA 10

Table3. 1: Concrete mix design based on design expert 2

Table4. 1:  Oxides composition of POFA 33

Table4. 2: Fine sand grain size distributions from sieve analysis 34

Table4. 3: Granite size distributions from sieve analysis 35

Table4. 4: specific gravity of cement and POFA 35

Table4. 5: Compressive strength at 7 days of curing age 36

Table4. 6: Compressive strength for 28 days curing age 40

Table4. 7: Compressive strength for 56 days curing age 44

Table4. 8: Compressive strength for 90 days curing age 46

Table4. 9summary of compressive strength (n/mm2) at different POFAmix ratio 49

Table 4. 10: Regression analysis for 7 days age concrete 50

Table 4. 11: Regression analysis for 28 days age concrete 50

Table 4. 12:  Regression analysis for 56 days age concrete 51

Table 4. 13: Regression analysis for 90 days age concrete 51

Table 4. 14: Analysis of variance for compressive strength 51

LIST OF FIGURES

Figure 2. 1: Strength versus UPV 9

Figure 2. 2: Compressive strength versus POFA replacement percentage 12

Figure 2. 3: Strength activity index of POFA mortar 13

Figure 2. 4: Relationship between UPV and replacement percentage 14

Figure 2. 5: Slump flow against POFA percentage 16

Figure 2. 6: Relationship between porosity and POFA content 17

Figure 2. 7: Relationship between strength and porosity of 80% content of POFA mortar 18

Figure 2. 8: relationship between permeability and replacement level of POFA 19

Figure 3. 1: Map of Maiduguri town showing Ramat Polytechnic 22

Figure 3. 2: Granite 23

Figure 3. 3 Palm oil kernel and ash 25

Figure 3. 4: sieve arrangement 26

Figure 3. 5: POFA replacement percentage (25% - 35%) 29

Figure 3. 6: Granite replacement percentage (0% - 100%) 29

Figure 3. 7: Cubes cast and curing 30

Figure 3. 8: Compressive strength test- 32

Figure 4. 1: Graph for grain size distribution for fine sand 34

Figure 4. 2: Graph for grain size distribution for granite 35

Figure 4. 3: Compressive strength vs granite and POFA at 7 days curing age 37

Figure 4. 4: Slump height vs granite and POFA at 7 days curing age 38

Figure 4. 5: Predicted and actual compressive strength at 7 days curing age 39

Figure 4. 6: Predicted and actual slump height at 7 days curing age 39

Figure 4. 7: Compressive strength vs granite and POFA at 28 days curing age 41

Figure 4. 8: Sump height vs granite and POFA at 28 days curing age 42

Figure 4. 9: Predicted and actual compressive strength at 28 days curing age 43

Figure 4. 10: Predicted and actual slump height at 28 days curing age 44

Figure 4. 11: Compressive strength vs granite and POFA at 56 days curing age 45

Figure 4. 12: Slump height vs granite and POFA at 56 days curing age 46

Figure 4. 13: Compressive strength vs granite and POFA at 90 days curing age 47

Figure 4. 14: Slump height vs granite and POFA at 90 days curing age 48

Figure 4. 15: Predicted and actual compressive strength at 28 days curing age 48

Figure 4. 16: Predicted and actual slump height at 28 days curing age 49

CHAPTER ONE

INTRODUCTION

1.1 Background of the study

Concrete is regarded as the primary and widely used construction ingredient around the world in which cement is the key material. However, large scale cement production contributes greenhouse gases both directly through the production of CO2 during manufacturing and also through the consumption of energy (combustion of fossil fuels). Moved by the economic and ecological concerns of cement, researchers have focused on finding a substitution of cement over the last several years. In order to address both the concerns simultaneously many attempts have been made in the past to use materials available as by product or waste. This is due to the fact that the use of by product not only eliminates the additional production cost, but also results in safety to the environment. Hence, the development and use of blended cement is growing rapidly in the construction industry mainly due to considerations of cost saving, energy saving, environmental protection and conservation of resources.

      A number of investigations have been carried out with Palm oil fuel ash (POFA), an agro-waste ash, as potential replacement of cement in concrete. Sata et al. (2004) found compressive strength of 81.3, 85.9, and 79.8 MPa at the age of 28 days by using improved POFA with a reduced particle size of about 10 microns in concrete as replacement of 10%, 20% and 30% of cement respectively. They also reported highest strength at 20% replacement level. Tangchirapat [2009] observed the compressive strengths of ground POFA concrete in the range of 59.5–64.3 MPa at 28 days of water curing and with 20% replacement it was as high as 70 MPa at the end of 90 days of water curing. However, the drying shrinkage and water permeability were noted to be lower than that of control concrete with improved sulphate resistance. Past researchers also depict that both ground and un-ground POFA increase the water demand and thus decrease the workability of concrete. However, ground POFA has shown a good potential for improving the hardened properties and durability of concrete due to its satisfactory micro-filling ability and pozzolanic activity. Palm Oil Fuel Ash (POFA) is known as the by-product form from the incinerationof the palm oil fibers, shells, and empty fruit bunches in the biomass thermal power plant to generate energy. However, it was found that 5 % of the residue was then produced as the result of combustion and the wastes are then managed by disposing as landfill materials which lead to environmental hazards eventually. As stated by Aprianti et al. (2015), POFA is tagged as the environmental disruption pollutant which ends up in the atmosphere without being utilized in 20th and 21stcentury, if compared to other types of palm oil by-products.

      Over the past several decades, attempt has been made to use several waste and by product material produced by the industries as potential partial replacement of cement in concrete. Investigations have been carried out through replacing part cement with industrial and other wastes such as Silica fume, ground granulated blast furnace slag, bagasse ash, rice husk ash, palm oil fuel ash, Paper mill ash, Wheat straw ash, Wallostonite, Metakaolin and many more (Karim et al., 2014). The use of these materials in concrete has significant benefits from environmental and economic stand point in comparison to traditional cement. In order to promote the utilization of POFA, many researchers established the researches regarding the POFA as the Supplementary Cementitious (SCM) in either concrete or mortar. The properties and performances of the finished products were examined and the researchers commented that the utilization of the POFA as a supplementary materials of cement is suitable. This is because the ash can increase the engineering and durability properties of either concrete or mortar. Karim et al., (2011) discovered that concrete produced using a particular level of POFA replacement achieved same or more strength as compared to OPC concrete. No significant strength reduction of concrete was observed up to about 30% replacement of POFA. Safiuddin et al., (2012) observed that the use of POFA is limited to a partial replacement, ranging from 0-30% by weight of the total cementitious material in the production of concrete. Indeed, the partial replacement has a beneficial effect on the general properties of concrete as well as cost. Sata et al., (2010) investigated that the strength development of POFA concretes with w/c ratios of 0.50, 0.55, and 0.60 tended to be in the same direction. At early ages, concretes containing POFA as a cement replacement of 10, 20, and 30% had lower strength development than control concretes while at later age 28 days, the replacement at rates of 10 and 20% yielded higher strength development. Mohammed Hussin and Awal., (2009) studied concrete replaced with POFA with a water to binder ratio of 0.45, were seen to develop strength exceeding the design strength of almost 60MPa at 28-day. Hussin et al., (2009) discovered that inclusion of 20% POFA would produce concrete having highest strength as compared to any other replacement level. Ahmad et al., (2008) studied that one of the potential recycles material from palm oil industry is palm oil fuel ash which contains siliceous compositions and reacted as pozzolans to produce a stronger and denser concrete.  Pozzolanic material has little or no cementing properties. However, when it has a fine particle size, in the presence of moisture it can react with calcium hydroxide at ordinary temperatures to provide the cementing property. Ahmad et al., (2008) reported that the chemical composition of POFA contains a large amount of silica and has high potential to be used as a cement replacement. Hussin et al., (2009) have found that POFA can be used in the construction industry, specifically as a supplementary cementitious material in concrete. Hussin et al., (2009) studied the compressive strength of concrete containing POFA. The results revealed that it was possible to replace at a level of 40% POFA without affecting compressive strength. The maximum compressive strength gain occurred at a replacement level of 30% by weight of binder. Karim et al., (2011) investigated that replacing 10–50% ash by weight of cementitious material in blended cement had no significant effect on segregation, shrinkage, water absorption, density, or soundness of concrete.

1.2 Scope

 Ordinary Portland Cement (OPC) concrete i.e. concrete with 100% OPC and ordinary gravel as control, and concrete with 25% - 35% POFA replacement and granite-gravel of 0% - 100% replacement having uniform water/binder (w/b) ratios of 0.5 and mixes ratio of 1:2:4 were used. Curing ages of 7 days, 28 days, 56 days and 90 days were considered. 

1.4 Justification

      Utilizing Palm Oil Fuel Ash (POFA) in concrete mix is a major way of turning waste to wealth. Gravel as an aggregate is cheaper than granite. Thus, obtaining an optimum combination of these materials in achieving a maximum compressive strength in concrete will go a long way in helping the construction industry.

1.5 Statement of Problem

      Large scale cement production contributes to greenhouse gases both directly through the production of CO2 during manufacturing and also through the consumption of energy. Therefore, this study examines the suitability of Palm Oil Fuel Ash (POFA) replacement with cement as Supplementary Cementing Materials. One of the potential recycle materials from palm oil industry is palm oil fuel ash which contains siliceous compositions and reacted as pozzolans to produce a stronger and denser concrete

1.6 Aim

To determine the mechanical properties of Palm Oil Fuel Ash (POFA). To address the aim, the following objectives were identified:

1.7 Objectives

1. To determine concrete compressive strength of granite-gravel concrete at varying replacement of Palm Oil Fuel Ash (POFA) at different curing ages.

2. To establish an optimum replacement of Palm Oil Fuel Ash (POFA) in granite-gravel blended.

.

EVALUATION OF MECHANICAL PROPERTIES OF PALM OIL FUEL ASH (POFA) BLENDED – GRANITE - GRAVEL CONCRETE



TYPE IN YOUR TOPIC AND CLICK SEARCH.






RESEARCHWAP.ORG

Researchwap.org is an online repository for free project topics and research materials, articles and custom writing of research works. We’re an online resource centre that provides a vast database for students to access numerous research project topics and materials. Researchwap.org guides and assist Postgraduate, Undergraduate and Final Year Students with well researched and quality project topics, topic ideas, research guides and project materials. We’re reliable and trustworthy, and we really understand what is called “time factor”, that is why we’ve simplified the process so that students can get their research projects ready on time. Our platform provides more educational services, such as hiring a writer, research analysis, and software for computer science research and we also seriously adhere to a timely delivery.

TESTIMONIES FROM OUR CLIENTS


Please feel free to carefully review some written and captured responses from our satisfied clients.

  • "Exceptionally outstanding. Highly recommend for all who wish to have effective and excellent project defence. Easily Accessable, Affordable, Effective and effective."

    Debby Henry George, Massachusetts Institute of Technology (MIT), Cambridge, USA.
  • "I saw this website on facebook page and I did not even bother since I was in a hurry to complete my project. But I am totally amazed that when I visited the website and saw the topic I was looking for and I decided to give a try and now I have received it within an hour after ordering the material. Am grateful guys!"

    Hilary Yusuf, United States International University Africa, Nairobi, Kenya.
  • "Researchwap.org is a website I recommend to all student and researchers within and outside the country. The web owners are doing great job and I appreciate them for that. Once again, thank you very much "researchwap.org" and God bless you and your business! ."

    Debby Henry George, Massachusetts Institute of Technology (MIT), Cambridge, USA.
  • "Great User Experience, Nice flows and Superb functionalities.The app is indeed a great tech innovation for greasing the wheels of final year, research and other pedagogical related project works. A trial would definitely convince you."

    Lamilare Valentine, Kwame Nkrumah University, Kumasi, Ghana.
  • "I love what you guys are doing, your material guided me well through my research. Thank you for helping me achieve academic success."

    Sampson, University of Nigeria, Nsukka.
  • "researchwap.com is God-sent! I got good grades in my seminar and project with the help of your service, thank you soooooo much."

    Cynthia, Akwa Ibom State University .
  • "Sorry, it was in my spam folder all along, I should have looked it up properly first. Please keep up the good work, your team is quite commited. Am grateful...I will certainly refer my friends too."

    Elizabeth, Obafemi Awolowo University
  • "Am happy the defense went well, thanks to your articles. I may not be able to express how grateful I am for all your assistance, but on my honour, I owe you guys a good number of referrals. Thank you once again."

    Ali Olanrewaju, Lagos State University.
  • "My Dear Researchwap, initially I never believed one can actually do honest business transactions with Nigerians online until i stumbled into your website. You have broken a new legacy of record as far as am concerned. Keep up the good work!"

    Willie Ekereobong, University of Port Harcourt.
  • "WOW, SO IT'S TRUE??!! I can't believe I got this quality work for just 3k...I thought it was scam ooo. I wouldn't mind if it goes for over 5k, its worth it. Thank you!"

    Theressa, Igbinedion University.
  • "I did not see my project topic on your website so I decided to call your customer care number, the attention I got was epic! I got help from the beginning to the end of my project in just 3 days, they even taught me how to defend my project and I got a 'B' at the end. Thank you so much researchwap.com, infact, I owe my graduating well today to you guys...."

    Joseph, Abia state Polytechnic.
  • "My friend told me about ResearchWap website, I doubted her until I saw her receive her full project in less than 15 miniutes, I tried mine too and got it same, right now, am telling everyone in my school about researchwap.com, no one has to suffer any more writing their project. Thank you for making life easy for me and my fellow students... Keep up the good work"

    Christiana, Landmark University .
  • "I wish I knew you guys when I wrote my first degree project, it took so much time and effort then. Now, with just a click of a button, I got my complete project in less than 15 minutes. You guys are too amazing!."

    Musa, Federal University of Technology Minna
  • "I was scared at first when I saw your website but I decided to risk my last 3k and surprisingly I got my complete project in my email box instantly. This is so nice!!!."

    Ali Obafemi, Ibrahim Badamasi Babangida University, Niger State.
  • To contribute to our success story, send us a feedback or please kindly call 2348037664978.
    Then your comment and contact will be published here also with your consent.

    Thank you for choosing researchwap.com.