DESIGN AND PRODUCTION OF CEILING BOARD USING PLASTER OF PARIS (POP) GYPSUM MATERIAL


DESIGN AND PRODUCTION OF CEILING BOARD USING PLASTER OF PARIS (POP) GYPSUM MATERIAL  

ABSTRACT

This project, Design and production of ceiling board using Plaster of Paris (POP) Gypsum materials. Gypsum is basically the raw material required in the manufacturing Plaster of Paris (POP) which posses an outstanding property  and a good material for producing ceiling board.

The materials procured for the project are plaster of Paris, fiber, water and mould. The equipment used for the project are scrapper, measuring tape, mixing bowl, bucket. Firstly, water was poured into the container (mixing bowl) and plaster of Paris sprinkled, two minutes was waited for absorption and then the mortar was mixed with hand and shaked vigorously to obtain a fully homogeneous mixture and thereafter the mortar was sprayed on the mould and fiber was added which serves as reinforcement.

Water absorption test was carried out on the sample and the result indicated that plaster of Paris (POP) ceiling board has an average 8.4 percent water absorptivity compare to Asbestos with 0.5 percent. Therefore plaster of paris (POP) ceiling board absorb water readily in case there is water leakage of the roof. Flexural strength test was carried out and the result obtained showed that plaster of paris (POP) ceiling board has a mean flexural strength of 11.4 N/mm2 and Asbestos has an average flexural strength of about 1.00 N /mm2.

 To this end, it is proved that plaster of paris (POP) ceiling board posses sufficient strength and it is durable for Civil Engineering works.

TABLE OF CONTENTS

Title page i

Certification ii

Dedication iii

Acknowledgement iv

Abstract v

Table of contents vi

List of plates ix

List of tables x

CHAPTER ONE

1.0 Introduction 1

1.1 Statement of problem 3

1.2 Aim and Objectives 3

1.3 Justification of study 3

1.4 Scope of the study 4

CHAPTER TWO

2.0 Literature Review 5

2.1 History of Gypsum 6

2.2 Old use of Gypsum 7

2.3 Modern use of Gypsum 8

2.4 Gypsum Credential 9

2.5 Gypsum product and its unique properties 10

2.5.1 Fire Resistance 10

2.5.2 Acoustic Properties 11

2.5.3 Thermal Properties 11

2.5.4 Aesthetics and Design 12

2.5.5 Sound Isolation Properties 12

2.6 Manufacture of plaster from Gypsum 12

2.7 Physical Properties of Gypsum 13

2.8 Chemical Properties of Gypsum 14

2.9 Survey on Hemp core fiber 14

CHAPTER THREE

3.0 Methodology 17

3.1 Procurement of Materials 17

3.2 Equipment used for the project 17

3.3 Preparation of Mould 17

3.4 Preparation of separator 18

3.5 Mixing of Aggregate 18

3.6 Casting 18

3.7 Demoulding 19

3.8 Water Absorption Test 19

3.9 Flexural Strength Test 20

CHAPTER FOUR

4.0 Result and Discussion 21

4.1 Plates 21

4.2 Tables and Calculation 32

CHAPTER FIVE

5.0 Conclusion and Recommendation 34

5.1 Conclusion 34

5.2 Recommendation 35

REFERENCES 36

LIST OF PLATES

Plate 4.1 Mould used for the project 21

Plate 4.2 Application of separator 21

Plate 4.3 Mixing of Aggregate 22

Plate 4.4 Casting process 1 23

Plate 4.5 Casting process 2 24

Plate 4.6 Casting process 3 25

Plate 4.7 waiting for the sample to set 26

Plate 4.8 Demoulding 28

Plate 4.9 The Sample 30

Plate 4.10 Weighing of the sample 31

LIST OF TABLES

Table 4.1 Water Absorption test Result 32

Table 4.2 Flexural Strength test Result 33

CHAPTER ONE

1.0     INTRODUCTION

This project deals with the design and production of ceiling board using POP gypsum materials. Plaster of Paris (POP) which is calcium sulphate with half molecule of water of crystallization (CaSO4.1/2H20)  and  hygroscopic characteristic obtained by duly  calcined the material that is Gypsum (CaSO4.2H20). It possess an outstanding property of setting and subsequent hardening when mixed with water (Smith, 1896).

Gypsum is basically the raw material require to manufacture Plaster of Paris. This is cleaned and washed for removal of impurities, dried in sunlight and then pulverized. Gypsum powder are calcined in a rotary drum calcinatory using light diesel oil/firewood/coal as fuel. The low pressure burner is sufficient to reach the calcinations temperature range from 160oc to 180oc.The process of calcinations is done over a period of about 2 hours so that one – halves molecule of water is removed to obtain the required properties after cooling, the calcined powder is passed through 150 mesh and packed in airtight polythene lined bags.

Modern Gypsum board has it predecessor a product called “sackett board”. A composite material that was made of layer of thin plaster placed between four piles of wool felt paper. Sackett board was  patented in 1894,  By  Augustine Sackett, The man generally considered to be the grandfather of gypsum board manufacturing industry.

Prior to 1894, Gypsum had been used for thousand of years as building material and as an architectural detailing element. The first use of gypsum in building construction appears to occurred in 3700BC, when an Egyptian used gypsum blocks and plaster applied over woven straw lath in the building of the pyramid of cheops.

A French chemist (Lavoiser, 1710), Analysed the chemical make up  of gypsum, his work and subsequent research by a group of his contemporary chemists coupled with the discovery and mining of huge reserve of gypsum near Paris leads to the wholesale use of plaster of Paris as a building material.

Plaster of Paris is extensively used in ceramics industry for preparation of models and moulds. It is also used as main raw material in the manufacture of toy and statues, chalk, crayon, gypsum plaster board and decorative picture frame besides wide range of application in interior decoration of building and other establishment (Alfred, 1896).

As there is growing building construction activities and advancement in technology, POP gypsum board are used in home and  offices  and  indeed  all  type of  building  where  people congregate such as schools, halls, churches, mosques, airports e.t.c.

POP gypsum ceiling board provides more aesthetic outlook, offer adequate resistance to heat and sufficient resistance to fire.

1.1 STATEMENT OF PROBLEM

Recent  studies indicate that asbestos ceiling contains hazardous material from the health point of view. Prolonged inhalation of asbestos fiber can cause lung cancer, mesothelioma, asbestosis. Therefore it has been banned from use in many developed country due to the chrysotile content.

To this end, there is need for alternative ceiling material which is durable, reliable and affordable.

1.2 AIM AND OBJECTIVES OF THE STUDY    

The aim of this project is to design and produce  ceiling board using POP gypsum materials

The objectives of the study is highlighted below :-

⦁ To produce durable lightweight building material for ceiling

⦁ To determine the strength of the ceiling board.

⦁ To determine it durability.

⦁ To determine the water absorption capacity.

1.3 JUSTIFICATION OF THE STUDY

The use of gypsum ceiling board for ceiling finishing should be adopted and improved because the problems associated with asbestos, which have been used as ceiling finishes for years but with the use of POP gypsum material as ceiling finishes which offers sufficient sound insulation and considerable absorption of heat from the roof and hence provide employment opportunity to the producer.

1.4 SCOPE OF THE STUDY

The scope and limitation of this project is basically the design and production of ceiling board using  POP  gypsum material. In this project, water absorption test and flexural strength test was carried out to determine the water capacity, strength and durability of the sample made up of composite quantity of POP plaster, water and fibre (villas) when subjected to loading.

.

DESIGN AND PRODUCTION OF CEILING BOARD USING PLASTER OF PARIS (POP) GYPSUM MATERIAL



TYPE IN YOUR TOPIC AND CLICK SEARCH.






RESEARCHWAP.ORG
Researchwap.org is an online repository for free project topics and research materials, articles and custom writing of research works. We’re an online resource centre that provides a vast database for students to access numerous research project topics and materials. Researchwap.org guides and assist Postgraduate, Undergraduate and Final Year Students with well researched and quality project topics, topic ideas, research guides and project materials. We’re reliable and trustworthy, and we really understand what is called “time factor”, that is why we’ve simplified the process so that students can get their research projects ready on time. Our platform provides more educational services, such as hiring a writer, research analysis, and software for computer science research and we also seriously adhere to a timely delivery.

TESTIMONIES FROM OUR CLIENTS


Please feel free to carefully review some written and captured responses from our satisfied clients.

  • "Exceptionally outstanding. Highly recommend for all who wish to have effective and excellent project defence. Easily Accessable, Affordable, Effective and effective."

    Debby Henry George, Massachusetts Institute of Technology (MIT), Cambridge, USA.
  • "I saw this website on facebook page and I did not even bother since I was in a hurry to complete my project. But I am totally amazed that when I visited the website and saw the topic I was looking for and I decided to give a try and now I have received it within an hour after ordering the material. Am grateful guys!"

    Hilary Yusuf, United States International University Africa, Nairobi, Kenya.
  • "Researchwap.org is a website I recommend to all student and researchers within and outside the country. The web owners are doing great job and I appreciate them for that. Once again, thank you very much "researchwap.org" and God bless you and your business! ."

    Debby Henry George, Massachusetts Institute of Technology (MIT), Cambridge, USA.
  • "Great User Experience, Nice flows and Superb functionalities.The app is indeed a great tech innovation for greasing the wheels of final year, research and other pedagogical related project works. A trial would definitely convince you."

    Lamilare Valentine, Kwame Nkrumah University, Kumasi, Ghana.
  • "I love what you guys are doing, your material guided me well through my research. Thank you for helping me achieve academic success."

    Sampson, University of Nigeria, Nsukka.
  • "researchwap.com is God-sent! I got good grades in my seminar and project with the help of your service, thank you soooooo much."

    Cynthia, Akwa Ibom State University .
  • "Sorry, it was in my spam folder all along, I should have looked it up properly first. Please keep up the good work, your team is quite commited. Am grateful...I will certainly refer my friends too."

    Elizabeth, Obafemi Awolowo University
  • "Am happy the defense went well, thanks to your articles. I may not be able to express how grateful I am for all your assistance, but on my honour, I owe you guys a good number of referrals. Thank you once again."

    Ali Olanrewaju, Lagos State University.
  • "My Dear Researchwap, initially I never believed one can actually do honest business transactions with Nigerians online until i stumbled into your website. You have broken a new legacy of record as far as am concerned. Keep up the good work!"

    Willie Ekereobong, University of Port Harcourt.
  • "WOW, SO IT'S TRUE??!! I can't believe I got this quality work for just 3k...I thought it was scam ooo. I wouldn't mind if it goes for over 5k, its worth it. Thank you!"

    Theressa, Igbinedion University.
  • "I did not see my project topic on your website so I decided to call your customer care number, the attention I got was epic! I got help from the beginning to the end of my project in just 3 days, they even taught me how to defend my project and I got a 'B' at the end. Thank you so much researchwap.com, infact, I owe my graduating well today to you guys...."

    Joseph, Abia state Polytechnic.
  • "My friend told me about ResearchWap website, I doubted her until I saw her receive her full project in less than 15 miniutes, I tried mine too and got it same, right now, am telling everyone in my school about researchwap.com, no one has to suffer any more writing their project. Thank you for making life easy for me and my fellow students... Keep up the good work"

    Christiana, Landmark University .
  • "I wish I knew you guys when I wrote my first degree project, it took so much time and effort then. Now, with just a click of a button, I got my complete project in less than 15 minutes. You guys are too amazing!."

    Musa, Federal University of Technology Minna
  • "I was scared at first when I saw your website but I decided to risk my last 3k and surprisingly I got my complete project in my email box instantly. This is so nice!!!."

    Ali Obafemi, Ibrahim Badamasi Babangida University, Niger State.
  • To contribute to our success story, send us a feedback or please kindly call 2348037664978.
    Then your comment and contact will be published here also with your consent.

    Thank you for choosing researchwap.com.