THE PRODUCTION OF HIGH-QUALITY FOAM


THE PRODUCTION OF HIGH-QUALITY FOAM

                                                        ABSTRACT:

The production of high-quality foam was carried.  The actualization of the production of polyurethane (fibre) foam was made possible by using the components / chemical raw materials such as polyol (polyurethes resin).  TDI (toluene di-Iso-cyanate, methylane chloride (MC)-(CH2CL).  Silicon oil, stannous octoate, calcum carbonate and water.

As a result of chemistry of polyurethane foams, properties of foams and fibre materials (physical, chemical, thermal and mechanical properties) gotten from the literature, review including the functions and reactions of the components proper formulation was made and conversions / translation to actual weights also done which lead to the production of the desired product. The experiment was done at ambient temperature of 320c following the normal procedures.

The foam produced is of very high density, good quality, durable and profitable. The densities of the various samples are 35kg/m3 and 40kg/m3.

As a result of poor storage conditions of the chemicals mentioned above here in the pilot plant, the stipulated and specified environmental conditions, there is a slight deviation of the foam from the international standard specification of 155. The foam produced are measured to standard and can be used for applied to any field of engineering and technology. They can be used for any purpose and is expected to last longer depending on the handling.                       TABLE OF CONTENTS

Content                                            Page

Title page    -    -    -    -    -    -    -    -    -    -    i

Approval    -    -    -    -    -    -    -    -    -    -    ii

Dedication    -    -    -    -    -    -    -    -    -    -    iii

Acknowledgement    -    -    -    -    -    -    -    -    -    iv

Abstract    -    -    -    -    -    -    -    -    -    -    v

Chapter One

1.0    Introduction

1.1    Problem statement

1.2    Aims and objectives of the project

Chapter two

2.0    Literature Review

2.1    Origin of foam

2.2    Structure of polyurethane

2.3    Properties of polyurethane foam

2.4    Classification of polyurethane

2.5    Flexible foam

2.6    Rigid foam

2.7    Basic chemistry of foam production

2.8    Polyurethane chemicals and functions

2.8.1    Man chemicals

2.8.2    Blowing agents

2.8.3    Catalyst

2.9    Foam stabilizers

2.10    Making / Agitation

2.11    Characteristic features of methyl come chloride

2.12    Some possible faults, causes and their remedies.

2.13    Characteristics of fibre foams

2.14    Physical properties of foam polyurethane

2.15    Thermal properties of polyurethane foams

2.16    Foam fibres applications

2.17    Factors that causes defect during process

Chapter three

3.0    Foam formulation

3.1    The roles of chemicals in foaming reactors

3.2    Determination of Chemical consumption rates

3.2.1    Water 

3.2.2    Tohiene DI – Isocyanate

3.2.3    Blowing Agents

3.2.4    Schlone

3.2.5    Amine

3.2.6    Stannous actuate

3.2.7    Colorant

3.3    Summary  of the formulation

Chapter four

4.0    Production procedure / Analyses

4.1    Essential Raw Materials Used

4.2 Procedures/methods

4.3    Experimental Results / Analysis

4.4    General Thermal properties

4.5    Chemical properties

4.6    Optical properties

4.7    Electrical properties

4.8    Permanence and service properties

4.9    Characteristic Test

4.10    Sampling and conditioning

4.11    Storage and Handling of urethane raw materials

Chapter five

5.0    Discussion

Chapter six

6.0    Conclusion

6.1    Recommendation

6.2    Cost Analysis

6.3    References                         CHAPTER ONE:

INTRODUCTION -

Polyurethane foam otherwise known as expanded polymer products are group of materials developed as gotten by there action between alcohol with two or more reactive hydroxyl group per molecule. This branch of polymer technology are finding increasing applications in many field of engineering including arts and sciences. Foam was discovered as a result of man’s strong desire in quest to his environment. There are many kinds of foam based on their inherent features such as high rigidity, stiffness per unit weight of polymer thermal and acoustical insulating properties. Cushioning properties or shock absorbency characteristics, low internal stresses of foamed mouldings and ease of forming. As a result of these, extensive range of materials and manufactured articles with different applications are produced from polymer.

The three types of foams are flexible, rigid and semi-rigid foams. It’s used in many structural applications where they form light weight care. Cellular products contains gas usually air, within their structures, they have lower thermal conductivity and are therefore good thermal insulants. Because foams able to dissipate energy reversible and storage capacity. They are used in cushions and are exploited in upholstery bedding laminated clothing and packaging.

Every polymer can be produced in cellular form but these that have been extensively used includes, polyurethane, polystyrene, polyethylene, polyethylene, poly- (vinyl chloride), cellulose acetate, phenolies epoxides, urea-formaldehyde resins, silicones naturally rubber e.g. later from which is made from liquid starting material; sponge rubber and expanded rubber, both made from solid materials.  Cellular plastics are basically of two types, flexible foam and rigid or structural foam.  They may also be classified according to density as low density foam (< 100kg/m3), medium density foam (600-1000kg/m3).

Cellular polymers may have either an open-cell structure in which the cells are closed separate units (unicellular foams) and may contain gas or air.  Materials with open-cell structures have high permeability’s to liquid and gases but because closed – cell structures contains air, their elastic moduli in compression are higher and they have the best thermal insulations.

Polyethylene foams can be produced by injection moulding or may be processed by special machines designed to measure the required ratio of chemical, mixing them together and dispense the reaction mixture in predetermined amounts.  There has been continuous development of machine for processing along side the development of polyethylene technology.

Based on the environmental impact and protechona, new dimensions to further challenges in the development of polyethylene technology has taken place which have contributed to the increasing application of polyethylene in our daily lives from foam resistant coating.

As a matter of facts, this research project is centered on flexible foam of higher density and characterization and different types of polymeric reactions could produce different materials like plastics rubber, filmos, fire surface coating and adhesive.  As a result of variation in reaction hydroxyl groups of alcohol and isocyanate, senies of polyethylene products have been produced.  This ranges from flexible soft and revilement material to hard, brittle and rigid.

Generally, four bare isocyanates and a range of polyol of different molecular weight and functionalities are used in the production of whole spectrum of polyethylene products/materials.

As the case may be, various types of foams with different characteristics features are produced by varying the medium, mixing ratio etc.

1.1    PROBLEM STATEMENT

Based on the fact that some raw materials are gotten from out petrochenueal industries/chemical industries, these unused materials are property channeled to effective use in producing polymer materials e.g. foam, such materials are toluenemdi-isocyanata, polyether, resin, polyol, etc.

1.2    AIMS AND OBJECTIVES OF THE PROJECT

This project/research is aimed at producing polyethylene foam that could be used or applied in various fields to satisfy human wants in Nigeria particularly and the world in general.

It is expected that if this research project is successful, a medium-layer scale industries would be established to best foam production.

Thirdly, an employment opportunity would be created for many Nigerians and would also bring foreign exchange to the country and also attract foreign investors to come into Nigeria.

.

THE PRODUCTION OF HIGH-QUALITY FOAM



TYPE IN YOUR TOPIC AND CLICK SEARCH.






RESEARCHWAP.ORG

Researchwap.org is an online repository for free project topics and research materials, articles and custom writing of research works. We’re an online resource centre that provides a vast database for students to access numerous research project topics and materials. Researchwap.org guides and assist Postgraduate, Undergraduate and Final Year Students with well researched and quality project topics, topic ideas, research guides and project materials. We’re reliable and trustworthy, and we really understand what is called “time factor”, that is why we’ve simplified the process so that students can get their research projects ready on time. Our platform provides more educational services, such as hiring a writer, research analysis, and software for computer science research and we also seriously adhere to a timely delivery.

TESTIMONIES FROM OUR CLIENTS


Please feel free to carefully review some written and captured responses from our satisfied clients.

  • "Exceptionally outstanding. Highly recommend for all who wish to have effective and excellent project defence. Easily Accessable, Affordable, Effective and effective."

    Debby Henry George, Massachusetts Institute of Technology (MIT), Cambridge, USA.
  • "I saw this website on facebook page and I did not even bother since I was in a hurry to complete my project. But I am totally amazed that when I visited the website and saw the topic I was looking for and I decided to give a try and now I have received it within an hour after ordering the material. Am grateful guys!"

    Hilary Yusuf, United States International University Africa, Nairobi, Kenya.
  • "Researchwap.org is a website I recommend to all student and researchers within and outside the country. The web owners are doing great job and I appreciate them for that. Once again, thank you very much "researchwap.org" and God bless you and your business! ."

    Debby Henry George, Massachusetts Institute of Technology (MIT), Cambridge, USA.
  • "Great User Experience, Nice flows and Superb functionalities.The app is indeed a great tech innovation for greasing the wheels of final year, research and other pedagogical related project works. A trial would definitely convince you."

    Lamilare Valentine, Kwame Nkrumah University, Kumasi, Ghana.
  • "I love what you guys are doing, your material guided me well through my research. Thank you for helping me achieve academic success."

    Sampson, University of Nigeria, Nsukka.
  • "researchwap.com is God-sent! I got good grades in my seminar and project with the help of your service, thank you soooooo much."

    Cynthia, Akwa Ibom State University .
  • "Sorry, it was in my spam folder all along, I should have looked it up properly first. Please keep up the good work, your team is quite commited. Am grateful...I will certainly refer my friends too."

    Elizabeth, Obafemi Awolowo University
  • "Am happy the defense went well, thanks to your articles. I may not be able to express how grateful I am for all your assistance, but on my honour, I owe you guys a good number of referrals. Thank you once again."

    Ali Olanrewaju, Lagos State University.
  • "My Dear Researchwap, initially I never believed one can actually do honest business transactions with Nigerians online until i stumbled into your website. You have broken a new legacy of record as far as am concerned. Keep up the good work!"

    Willie Ekereobong, University of Port Harcourt.
  • "WOW, SO IT'S TRUE??!! I can't believe I got this quality work for just 3k...I thought it was scam ooo. I wouldn't mind if it goes for over 5k, its worth it. Thank you!"

    Theressa, Igbinedion University.
  • "I did not see my project topic on your website so I decided to call your customer care number, the attention I got was epic! I got help from the beginning to the end of my project in just 3 days, they even taught me how to defend my project and I got a 'B' at the end. Thank you so much researchwap.com, infact, I owe my graduating well today to you guys...."

    Joseph, Abia state Polytechnic.
  • "My friend told me about ResearchWap website, I doubted her until I saw her receive her full project in less than 15 miniutes, I tried mine too and got it same, right now, am telling everyone in my school about researchwap.com, no one has to suffer any more writing their project. Thank you for making life easy for me and my fellow students... Keep up the good work"

    Christiana, Landmark University .
  • "I wish I knew you guys when I wrote my first degree project, it took so much time and effort then. Now, with just a click of a button, I got my complete project in less than 15 minutes. You guys are too amazing!."

    Musa, Federal University of Technology Minna
  • "I was scared at first when I saw your website but I decided to risk my last 3k and surprisingly I got my complete project in my email box instantly. This is so nice!!!."

    Ali Obafemi, Ibrahim Badamasi Babangida University, Niger State.
  • To contribute to our success story, send us a feedback or please kindly call 2348037664978.
    Then your comment and contact will be published here also with your consent.

    Thank you for choosing researchwap.com.